Yb:KGW

Ytterbium doped Potassium-Gadolinium Tungstate crystals - (Yb:KGd(WO4)2 or Yb:KGW) is an excellent laser gain material which has important advantages over the widely used Nd3+ doped materials. Its broad spectral emission band 1023-1060nm allows the generation of short (ps or fs) laser pulses. Its wide absorption spectrum at 980 nm and high absorption of pump radiation allow an efficient use of diode laser pumping. Compared with YAG used as hosts for Yb3+, KGW has the advantage of larger absorption cross section, which decreases the minimum pump intensity necessary to achieve transparency in the quasi-two-level system of ytterbium.


  • Introduction
  • Download
  • Feedback

Basic Properties of Yb:KGW:

Crystal structuremonoclinic
Point groupC2/c
Cell Parametersa = 8.09Å;  b = 10.43Å;  c = 7.588Å
 β=94.4°
Refractive index, at 1067 nmng=2.033;np=2.037;nm=1.986
Mohs hardness5
Density7.27g/cm3
Melting Point1075℃
Thermal conductivity @373K,W/cm/KK[100] = 0.026; K[010] = 0.038; K[001] = 0.034
Thermal expansion coefficient @373Kα[100] = 4 x 10-6 K-1; α[010] = 1.6 x 10-6 K-1;
 α [001] = 8.5 x 10-6 K-1
Lasing Wavelength1023-1060nm
Absorption band981nm(FWHM 3.7nm)
Fluorescent lifetime600μs(5% doping)

 

 

Specifications of Yb:KGW:

Orientation[010]
Standard Dopant concentration(at.%) 5%
Maximum length50mm
Length tolerance,mm+1.0/-0.0
Diameter tolerance,mm+/-0.1
Parallelism<30″
Perpendicularity<15′
Surface quality20/10
coatingAR-coated                

 


Dear visitors! Please submit your feedback information!

  • *Name:
  • Company:
  • *Tel:
  • *Email:
  • *Message:
  • *Code:


Copyright© CASTECH Inc. all rights reserved 闽ICP备12014619号 Copyright 2012-2017 51helpdesk.com

+-